KLEIBERIT 347.0 Artificial Resin Dispersion Glue 28 KGS
Window, Doors and Wood Bonding
Fields of application
● Bonding of laminates in a short cycle press ● Bonding of edges (cold bonding or with heated band) ● Assembly bonding and joint bonding ● Bonding of structural components ● Bonding of pilaster strips and ledges ● Post-forming, (see our separate data sheet 347.0 for post-forming) ● Bonding in shipbuilding KLEIBERIT 347.0 according to IMO FTP-Code Part 5 & Part 2/ approval according SeeBG (department vessel security) for international use according to Module B)
Approval No.: 118.286,production year Certified application quantity: 155 g/m²
Advantages
● Short setting time with cold and hot bonding up to 90°C ● Short open time, the glue is intended for fast press processing ● High yield Properties of the glue
Base : PVAC dispersion Specific weight : approx. 1.08 g/cm³ pH-value : approx. 5
Colour : white, transparent when dry Viscosity at 20ºC
spindle 6/20 rpm : 14.000 +/- 2.000 mPa.s Consistency : high viscosity, good application properties, also with machines Open Time : approx. 3 minutes
Press times :
Application Temp. Press time joint bonding 20°C 3-5 minutes joint bonding one sided 70°C 1-2 minutes pre-heated structural component bonding 20°C 4-5 minutes,
veneer edges bonding 80°C 1-1.5 minutes ledges bonding 20°C 1-3 minutes,
surface bonding (HPL-boards) 20°C 4-5 minutes, surface bonding (HPL-boards)
50°C 1-2 minutes, surface bonding (HPL-boards) 60°C approx. 1 minute

 

OMR 53.500 
Euro Glue 320.0 Surface Adhesive DIN EN 204 D2
Window, Doors and Wood Bonding
Fields of application
● Assembly bonding ● Veneer bonding ● Bonding of laminates ● Bonding of particle and MDF board ● Core production ● Joint and frame bonding of hard and soft wood
Advantages
● In bonding of veneers good results are obtained even after use of water based stains and wetting of veneer prior to bonding ● High bonding strength with hard and soft woods ● Favourable open time ● Short setting time with hot and cold bonding
Properties of the glue
Base : PVAC dispersion
Specific gravity : approx. 1.25 g/cm³, pH-value : approx. 7
Viscosity at 20ºC ,sp. 6/20 rpm : 15.000 +/- 2.000 mPa.s
Consistency : medium viscosity, good processing properties
Open Time : approx. 10 minutes
Pressing times:
Application Temp. Press time, Joint bonding 20°C approx. 10 min. Joint bonding, preheated on one side 50°C 3-5 minutes
Frame bonding 20°C 10-12 minutes, Veneer bonding 20°C 10-12 minutes
Veneer bonding 80°C 2-4 minutes, Surface bonding (HPL) 20°C 15-20 minutes
Surface bonding (HPL) 50°C 6-8 minutes

 

OMR 21.000 
KLEIBERIT 301.2 Water resistant PVAC 28 KGS Glue DIN EN 204
Window, Doors and Wood Bonding
Fields of use
● Bonding windows and doors ● Surface bonding of HPL boards ● Surface bonding during partition and element manufacture ● Bonding hard and exotic timbers, For the construction of stairs ● High frequency bonding Advantages ● Suitable for veneers ● As a single component glue - ready for use● Suitable for hot and cold bonding
Properties of the Glue
Base : PVAC dispersion, Density at 20°C : approx. 1.10 g/cm³, pH-value : approx. 3
Colour of glue : white, Viscosity at 20ºC, sp. 6/20 rpm : 15,000 ± 3,000 mPa·s
Consistency : medium viscous Pot life : approx. 24 hrs with hardener added, Open Time (at 20°C) : 6-10 minutes Chalk point : approx. +5°C
Press times:
Joint bonding at 20°C from 15 min, Joint bonding (pre-heated) at 50°C from 5 min
Joint bonding at 80°C from 2 min
Surface bonding HPL boards at 20°C from 15 - 20 min
Surface bonding HPL boards at 50°C from 5 min
Surface bonding at 80°C from 1 - 2 min
Depending on the type of wood and the surface properties
OMR 31.500 
KLEIBERIT 303 28 KGS Water-Resistant PVAC Adhesive water resista
Window, Doors and Wood Bonding
Fields of application
● Bonding of windows and doors ● Surface bonding of HPL-boards ● Surface bonding of partitions and parts ● Stair construction ● Bonding of laminates ● Bonding of tenon and finger joints ● Bonding of hard and exotic timbers ● High frequency bonding ● Bonding in shipbuilding
Advantages
● As single component glue - ready to use ● As two component glue - for highest demands ● Suitable for hot and cold bonding ● Short press times ● The composition of KLEIBERIT 303.0 complies with the FDA Guideline 21CFR § 175.105
Properties of the Glue
Base : PVAC dispersion, Density : approx. 1.10 g/cm³ , pH-value : approx. 3.0
Colour of the glue : white, Open time (at 20°C) : 6-10 minutes
spindle 6/20 rpm : 12,000 ± 2,000 mPa s, Pot life : approx. 24 hours with hardener
Open time (at 20°C) : 6-10 minutes (without hardener)
Consistency : medium viscosity, Viscosity at 20°C
spindle 6/20 rpm : 12,000 ± 2,000 mPa s, Chalk point : approx. +5°C
Application Temp. Press Time
Joint bonding 20°C from 15 minutes, Joint bonding (pre-heated) 50°C from 5 minutes
Joint bonding 80°C from 2 minutes ,
Surface bonding (HPL panels) 20°C 15-20 minutes
Surface bonding (HPL panels) 50°C approx. 5 minutes,
Surface bonding (HPL panels) 80°C 1-2 minutes

 

OMR 38.500 
KLEIBERIT 501 1 C PUR ADHESIVE 0.5KGS PLASTIC BOTTLE
Window, Doors and Wood Bonding

KLEIBERIT 501 is a single component
PUR adhesive for strong, gap-filling
bonds with high temperature resistance
according to DIN/EN 14257 (WATT 91)
and water resistance according to DIN/
EN 204 stress group D4.

Fileds of Application 

Bonding windows and doors, stairs, plywood to be used inside or outside (outsideuse with surface protection). Bonding mineral building boards, ceramic materials, concrete materials and hard foams.    

Preparation
The surfaces to be bonded must be climatised, clean, dry and free from dust and grease. Release agents must be completely removed.

KLEIBERIT 501.0
Viscosity at 20°C (mPa・s)
8000
Open time (20 °C) approx. 25 min.
Minimum press time
(20°C)
60 min. (40°C) 30 min. (60°C) 10 min.
Curing time 2-3 hours

 

OMR 2.400